Features:

• Polyester resin based on ortho-phthalic acid.

 

• Preaccelerated, enhanced shelf life, low styrene emission, thixotropic.

• Reactivity: Medium reactive.

• Low internal strain after curing.

 

• suitable for production of thick-walled parts wet on wet.

 

 

• Polyester resin Resinpal 1705 can be widely be used due to its good mechanical strength properties, especially if high impact strength is demanded

 

• Ready-to-use resin, for moulded parts off various types, e.g. boats, vehicle bodys, container etc;

 

• Polyester resin Resinpal 1705 is suitable for hand lay-up and spray-up-technique.

 

 

 

Application:

• The polyester resin Resinpal 1714 contains a peroxide indicator that after addition of ketone peroxides causes a color change from blue to brown green. The processor is thereby possible to control the addition of hardener.

• The polyester resin reinpal 1705 contains components that lead to a tack-free cure.

• The curin of the polyester resin Resinpal 1714 can take place at room temperature with the addition of MEKP-hardener). The tempetarture should be above 18 ° C.

 

Storage:

·         The resin should be stored in a dark and dry place at temperatures between 5°C and 25°C.

 

Technical data:

 

Flüssiger Agregatszustand

Non-Volatile Matter DIN 55671

non-volatile matter [%] 53 - 57 (120 °C; 5 min; 0,8 g)

Dynamic Viscosity DIN EN ISO 3219

Dynamic viscosity [mPa.s] 190 - 290 (500 1/s; 23 °C)

Dynamische Viskosität DIN EN ISO 3219

Dynamic viscosity [mPa.s] 690 - 1090 (2,5 1/s; 23 °C)

Gel Time (UP-Resins) DIN 16945 / 6.3.1.2

Gel time [min] 25 - 35

2% MEKP (33%) (20 °C)

Density (Liquids) DIN EN ISO 2811-2

Density [g/cm³] 1,08 ca. (20 °C)

Flash point DIN EN ISO 1523

Flash point [°C] 34